has been developed as an economical alternative to FEROBESTOS LA5 the acclaimed asbestos rotor vane material. The principal areas of use are in single and two stage vaccum pumps and compressors.

The information contained in this data sheet is presented in good faith. They are typical test results tested generally in accordance with BS 2782 and ASTM test methods and should not be used for specifications.



PROPERTIES UNITS F57
Density
g/cm3
1.2
Flexural Strength at Ambient

MPa

lbf/in2
165

23,925
Flexural Strength at 2000C
MPa
68
4 days @2000C Tested @2000C
lbf/in2
9,860
Flexural Modulus at Ambient

GPa

lbf/in2 x 106
5.6

0.81
Flexural Modulus at 2000C GPa 4.3
4 days @2000C Tested @2000C
lbf/in2 x 106 0.62
Compressive Strength

MPa

lbf/in2
380

55,100
Bond Strength
KN@ 7.9 thick 4.6
Scar Wear
mm 4.3
Coefficient of Thermal Expansion 106/
9
Maximum Continuous Operating Temperature
0C

200